B23R085 Silicon Steel

B23R085 B:Baosteel, R: Series of magnetic domains oriented silicon steel sheet.23 : Thickness 0.23mm, 23/100 for the product thickness, in mm., 085/100 indicates that the product core loss not greater than 0.85w / kg.

B35A360 Silicon Steel

B23R085 steel Mechanical Properties

Grade	tensile strength L（N/mm2）	Yield Strength L（N/mm2）	Elongation L（%）	Hardness HV1	Bending frequency (times)	Stacking factor（%）	tensile strength L（N/mm2）
B23P085	0.23	353	326	12	195	19	96.5

NOTE:. A detector according to GB / t228-2002, GB / T 19289-2003
b. above are typical values only for reference does not guarantee
c. L direction refers to the rolling direction

B23P085 electromagnetic performance standards

Grade	Nominal thickness（mm）	Theoretical density（kg/dm3）	Maximum core loss P17/50 (W/kg)	The minimum magnetic induction B8 （T）
B23P085	0.23	7.65	0.85	1.87

NOTE:. A detector according to GB / T 3655-2008 (G-series and P-series), GB / T3789-2008 (R Series)
b . G-series and P-series samples were rolling direction, and incubated for 2 hours at 800 ℃ magnetically eliminate stress after annealing treatment can be tested
c . P17/50 represents the maximum magnetic flux density of 1.7T, a frequency of 50Hz, the unit kg sample of core loss.

d . B50 represents the magnetic field intensity corresponding to the intensity of the magnetic induction 5000A / m when.

Silicon Steel overview