Stainless Steel 904l Plate sheets have notable resistance to warm seawater and along with resistance to chloride ion assault. The high resistance of Stainless Steel 904l Plate sheets towards stress related corrosion cracking Stainless Steel 904l Plate sheet is because of the presence of excessive amounts of nickel in its chemistry. In order to achieve maximum resistance to stress related corrosion cracking under critical environments, the Stainless Steel 904l Plate sheet needs to be solution treated following cold working.
UNS N08904 Stainless Steel 904l Plate sheet Mechanical Properties
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 7.95 g/cm3 | 1350 °C (2460 °F) | Psi – 71000 , MPa – 490 | Psi – 32000 , MPa – 220 | 35 % |
Corrosion Resistance:
Excellent resistance to warm seawater and chloride attack. The high resistance against stress corrosion cracking is due to the presence of high amounts of nickel in its composition.
The addition of copper to grade Stainless Steel 904l Plate sheet develops resistance to reducing agents including sulfuric acid in both aggressive and mild conditions.
Less resistant to nitric acid than grades 304L and 310L, which are free of molybdenum.
Should to be solution treated after cold working, for achieving maximum resistance to stress corrosion cracking in adverse environments.